| Item | Part A | Part B | |
Uncured |
Appearance | White&Black Flow | Translucent Flow |
| Viscosity(cps,25℃) | 6000-8000 | 20～50 | |
| Mixing ratio by weight | 6∶1 | ||
| Mixing ratio by volume | 4∶1 | ||
| Viscosity after mixing(cps,25℃) | 800-1800 | ||
| Potting Life（min，25℃） | 10-30 | ||
| Surface Molding time（hr，25℃） | 0.5-1.5 | ||
| Cured | Hardness(shore A) | 35-45 | |
| Shear strength ((MPa,Al-Al) | ≥1.7 | ||
| Dielectric Strength（kV/mm) | ≥20 | ||
| Break Elongation（%） | ≥80 | ||
| Tensile strength (MPa) | ≥1.0 | ||
| Volume Resistivity（Ω·cm） | ≥1.0×1015 | ||
| Specific Gravity (g/cm3) | 1.42±0.03 | ||
| Thermal Conductivity (W/m·K) | ≥0.5 | ||
| Temperature resistance（℃） | -60 to +200 | ||
| Flammability | UL 94-V0 | ||