Antas-362 is a one-component, moisture cure, low-viscosity silane-modified polyether sealant. It combines the advantages of both polyurethane and silicone sealants. It’s solvent-free, silicone oil-free, and NCO-free. It has excellent environmental performance and weather resistance and is an ideal replacement for polyurethane and silicone sealants
Get a Quote
Product manual
Antas-362 is a one-component, moisture cure, low-viscosity silane-modified polyether sealant. It combines the advantages of both polyurethane and silicone sealants. It’s solvent-free, silicone oil-free, and NCO-free. It has excellent environmental performance and weather resistance and is an ideal replacement for polyurethane and silicone sealants
Product feature
  • Low-viscosity:  manual sealant gun, easy to operate
  • Safe and environmental-friendly: solvent-free, NCO-free, low odor, low TVOC
  • Plastic bonding ability: can bond common interior substrates without primer
  • Surface modifiable: The surface of antas-362 can be colored, polished, and repaired, and it is not easy to stick to dust.
  • Strong climate resistance: excellent weather resistance
Main purpose
  • The sealing of automotive interior and non-structural bonding
  • Has excellent applicability for plastic substrates, and good adhesion to PVC, PP, PC, ABS, PMMA, and other materials.
Standards compliant
QGZJHG8-2018
Technical parameters
Test Items Q/GZJTHG 8-2018 Measured Value
Appearance Homogeneous, smooth paste; no bubbles, skinning, or impurity Homogeneous, smooth paste; no bubbles, skinning, or impurity
Density, g/cm3 Specified value ±0.1 1.6
Extrudability, ml/min ≥80 200
Sag degree Vertical, mm ≤3 0
Horizontal No deformation No deformation
Tack-free time, min ≤60 40
Curing speed, mm/24h ≥3.0 3.7
Solid content, % ≥95 99.2
Tensile Strength, MPa ≥1.8 2.0
Elongation at break, % ≥400 405
Shear strength, MPa ≥1.2 1.5
Tear Strength, kN/m ≥5.0 6.2
Hardness, Shore A 30~60 44
Low-temperature flexibility -40℃ no crack no crack
Peel Adhesion ≥90% CF 100% CF