JT-205M Water-Based Anticorrosion Top Coating

JT-205M Water-Based Anticorrosion Top Coating

JT-205M Water-Based Anticorrosion Top Coating
JT-205M Water-Based Anticorrosion Top Coating
JT-205M Water-Based Anticorrosion Top Coating
JT-205M Water-Based Anticorrosion Top Coating

JT-205M Water-Based Anticorrosion Top Coating

Model : JT-205M
Certification : ISO9001，ISO14001，ISO45001
Packaging : 20 kg/drum
Brand : JOINTAS
Place : Guangzhou, China
JT-205M is made from the film-forming material—water-based acrylic emulsion and added antirust slurry, rust inhibitors, water-based additives, and other materials. Anticorrosive pigment with high heavy metal content, such as mercury and lead, isn’t added.
Get a Quote
Product manual
JT-205M is made from the film-forming material—water-based acrylic emulsion, and added antirust slurry, rust inhibitors, water-based additives and other materials. Anticorrosive pigment with high heavy metal content ,such as mercury and lead, isn’t added.
Product feature
  • Low VOC, no pollution while construction, not flammable or explosive, safety for transportation and storage.
  • Excellent resistance to weather, UV, and color retention.
  • Quick-drying speed, excellent early water resistance.
Main purpose
  • Equipped with proper water-based primer, JT-205M is suitable for anticorrosion and antirust purpose on the surface of steel structural building and workshop, mechanical equipment and other metals. It exhibits excellent resistance to outdoor weather, UV and discoloration.
Technical parameters
Items Result
Lustre Flatting
Color Various, customized as color card
Volume solid content/% About 40
Theoretical coating rate 7.5m2/kg (measured as a 40-micron dry film)
Specific weight About 1.22kg/L
VOCs ≤50g/L
Flexibility ≤1mm
Tack free time ≤0.5h(25℃, humidity 50%)
Complete dry time ≤5h(25℃, humidity 50%)
Recoating time Minimum 4h, maximum 48h(25℃)
adhesion Level 0
Complete curing time 7d(25℃, humidity 50%)
Impact resistance 50cm