JT-413D Water-Based Two-component Epoxy Primer

JT-413D Water-Based Two-component Epoxy Primer

JT-413D Water-Based Two-component Epoxy Primer

JT-413D Water-Based Two-component Epoxy Primer

Model : JT-413D
Certification : ISO9001, ISO14001, ISO45001
Packaging : 20 kg/drum
Brand : JOINTAS
Place : Guangzhou, China
JT-413D is a new generation of water-based epoxy two-component anti-corrosion primer, which is made of water-based epoxy resin, amine curing agent, functional materials and related additives, with water as diluent. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added. The coating film has excellent resistance to water, salt water, salt spray and various chemical media. JT-413D can meet the requirements of most anti-corrosion fields.

Standard: HG/T 4759-2014
Get a Quote
Product manual
JT-413D is a new generation of water-based epoxy two-component anti-corrosion primer, which is made of water-based epoxy resin, amine curing agent, functional materials and related additives, with water as diluent. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added. The coating film has excellent resistance to water, salt water, salt spray and various chemical media. JT-413D can meet the requirements of most anti-corrosion fields.
Product feature
  • Low VOC，no pollution during construction
  • Non combustible or explosive, safe and convenient for transportation and storage
  • Excellent corrosion resistance and chemical medium resistance
  • Coating film has excellent resistanceto water, salt water and salt spray
Main purpose
  • JT-413D is suitable for antirust priming of metal surfaces such as large steel structures, engineering machinery and equipment, axle chassis and cast iron parts with high anti-corrosion performance requirements;
  • JT-413D can also be used in various onshore steel structures such as pipelines, power plants and chemical plants;
  • In addition to matching with the company's top coat, JT-413D can also be used as a matching primer for various solvent anti-corrosion coatings and industrial paints for other metal substrates.
Standards compliant
HG/T 4759-2014
Technical parameters
Items Result
Luster Matte
Color Iron red/ medium grey
Volume solid content/% 52±2
Theoretical coating rate 7.14 m2/kg (measured as a 50-micron dry film)
Specific weight 1.31±0.05 kg/L
Hardness H-2H
Tack free time 20min (25℃, humidity 50%)
Complete dry time 1.5h (25℃, humidity 50%)
Recoating time Minimum 6h, maximum 48h(25℃)
Complete curing time 7d(25℃, humidity 50%)
Adhesion Grade 0
Impact resistance 50kg·cm
Mixture ratio(Weight) Part A(main coating):Part B(curing agent)=5:1
Application period after mixture 6h(25℃)