NP-1002 Water-based Modified Silicone Acrylic Anticorrosive Top Coating

NP-1002 Water-based Modified Silicone Acrylic Anticorrosive Top Coating

NP-1002 Water-based Modified Silicone Acrylic Anticorrosive Top Coating

NP-1002 Water-based Modified Silicone Acrylic Anticorrosive Top Coating

Model : NP-1002
Certification : ISO9001, ISO14001, ISO45001
Brand : JOINTAS
Place : Guangzhou, China
NP-1002 use water-based silicone modified acrylic emulsion as the film forming material, with rust preventive pigment, rust inhibitor and nano functional additives added. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Get a Quote
Product manual
NP-1002 use water-based silicone modified acrylic emulsion as the film forming material, with rust preventive pigment, rust inhibitor and nano functional additives added. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Product feature
  • Excellent durability, ultraviolet resistance and self-cleaning functions, and can also prevent fading caused by acid rain
  • Good decorative effect, long-lasting and bright color
  • Excellent rust resistance, acid and alkali resistance, salt spray resistance, weathering resistance, water-based environmental protection
  • Firm adhesion, good maintenance and wide applicability
Main purpose
  • NP-1002 is applicable to metal surface coating of petrochemical oil tank outer wall, device, pipeline and equipment with high requirements for weather resistance and decoration effect;
  • Suitable for anti-corrosion top coating.
Technical parameters
Items Result
Luster Flat
Color White
Mass solid content(main coating) About 50%
Theoretical coating rate 0.20 kg/ m2(measured as a 50-micron dry film)
Tack free time ≤2h (25℃, humidity 50%)
Complete dry time ≤24h (25℃, humidity 50%)
Recoating time Minimum 4h, maximum 48h(25℃)
Specific weight About 1.20 kg/L