NP-1002G Water-based Acrylic Insulating and Anticorrosive Top Coating

NP-1002G Water-based Acrylic Insulating and Anticorrosive Top Coating

NP-1002G Water-based Acrylic Insulating and Anticorrosive Top Coating

NP-1002G Water-based Acrylic Insulating and Anticorrosive Top Coating

Model : NP-1002G
Certification : ISO9001, ISO14001, ISO45001
Brand : JOINTAS
Place : Guangzhou, China
NP-1002G is made of water-based acrylic emulsion as the film forming material, with titanium white powder, rust preventive and weatherproof pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Get a Quote
Product manual
NP-1002G is made of water-based acrylic emulsion as the film forming material, with titanium white powder, rust preventive and weatherproof pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Product feature
  • Excellent weather resistance, UV resistance and self-cleaning function.
  • Excellent near-infrared and visible light reflection performance. When used together with thermal insulation intermediate coating such as NP-1002Z, it can provide very excellent thermal insulation effect.
  • Excellent resistance to acid, salt water and salt spray, with wide applicability.
Main purpose
  • It is applicable to the outer surface of oil storage tank, oil pipeline, device and equipment with thermal insulation requirements, used as anti-corrosion thermal-insulating top coating.
Technical parameters
Items Result
Luster Matte
Color White
Mass solid content(main coating) About 54%
Theoretical coating rate 0.28 kg/ m2(measured as a 70-micron dry film)
Tack free time ≤2h (25℃, humidity 50%)
Complete dry time ≤24h (25℃, humidity 50%)
Recoating time Minimum 2h, maximum 48h(25℃)
Specific weight About 1.25 kg/L