NP-1002Z Water-based Acrylic Insulating and Anticorrosive intermediate Coating

NP-1002Z Water-based Acrylic Insulating and Anticorrosive intermediate Coating

NP-1002Z Water-based Acrylic Insulating and Anticorrosive intermediate Coating

NP-1002Z Water-based Acrylic Insulating and Anticorrosive intermediate Coating

Model : NP-1002Z
Certification : ISO9001, ISO14001, ISO45001
Brand : JOINTAS
Place : Guangzhou, China
NP-1002Z is made of waterbased acrylic emulsion as film forming material, adding rust preventive pigment, heat insulation pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Get a Quote
Product manual
NP-1002Z is made of waterbased acrylic emulsion as film forming material, adding rust preventive pigment, heat insulation pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Product feature
  • Excellent insulation, salt water and fog resistance, water-based environmental-friendly
  • Excellent heat insulation performance, low thermal conductivity, lasting and effective heat insulation effect
  • Firm adhesion, excellent supporting and construction property
Main purpose
  • It is applicable to the outer surface of oil storage tank, oil pipeline, device and equipment with thermal insulation requirements, used as anti-corrosion thermal-insulating intermediate coating.
Technical parameters
Items Result
Luster Flat
Color Iron Red
Mass solid content(main coating) About 50%
Theoretical coating rate 0.48 kg/ m2(measured as a 150-micron dry film)
Tack free time ≤2h (25℃, humidity 50%)
Complete dry time ≤24h (25℃, humidity 50%)
Recoating time Minimum 2h, maximum 48h(25℃)
Specific weight About 1.04 kg/L